DESCRIPTION
VSS-316L-17 is a lime-titania type stainless steel electrode which gives an extra low carbon and virtually free from spatter.
Because of extra low carbon content especially, the deposited metal has more excellent resistance to the intercystalline corrosion than that of ordinary 316 type.
Due to excellent properties at high temperature, it is widely used in various chemical industries. Peeling-off of the slag is very good.
APPLICATIONS
Welding of AlSl316L.
INSTRUCTIONS FOR WELDING
Clean off dust or oil from the welding area in order to prevent from decreasing the corrosion resistance caused by interblending carbon to the deposited metal.
Typical Chemical Composition of Weld Metal (%):
C |
Si |
Mn |
Cr |
Ni |
Mo |
0.034 |
0.38 |
1.68 |
19.12 |
12.25 |
2.27 |
Typical Mechanical Properties of Weld Metal:
Tensile Strength
N/mm2 (Ksi) |
Elongation
(%) |
567 (82) |
45 |
Size and Recommended Current Range (AC or DC +):
Diameter (mm) |
1.6 |
2.0 |
2.5 |
3.2 |
4.0 |
5.0 |
|
Length (mm) |
255 |
255 |
300 |
350 |
350 |
350 |
|
Ampere |
Flat |
20-50 |
20-50 |
50-80 |
70-110 |
100-150 |
130-180 |
V&OH |
15-45 |
15-45 |
45-75 |
65-105 |
95-140 |
- |
| |
|
|
|
|
|
|
|
|
|
|
|
|
Welding Positions:
FLAT, FILLET, VERTICAL UP, HORIZONTAL, OVERHEAD
APPROVALS: ABS
Packing:
EXPORT (1.6-2.5mm): 16 Kg corrugated box, with 4 units of 4 Kg plastic container.
EXPORT (3.2-5.0mm): 20 Kg corrugated box, with 4 units of 5 Kg plastic container.
LOCAL: 5Kg Special Paper Box with shrink wrapped plastic
Special requests on packing are accepted. |